Sheeting And Cladding

Sheeting And Cladding

Sheeting And Cladding

Sandwich panel

Rigid polyurethane foam, sandwiched by metal or flexible facings, is increasingly successful in meeting the requirements of the construction industry, emphasizing on cost effective system building and energy conversation. Their specific file of application covers the construction of industrial and commercial buildings, ware houses and cold storages, refrigerated transportation).

Polyurethanes are three dimensionally networked macro cellular thermosets as a result of a reaction between a multifunctional polyol and a multifunctional isocyamnate/MDI in the presence of a blowing agent and additives.

Sandwich panels offer a wide range of properties which are responsible for the increase demand of this unexcelled construction metal.

Neotech can supply sandwich panels in various thickness (35mm to 100mm), various facing combinations of pre painted steel and aluminium in thickness ranging from 0.25mm to 1.0mm and in different colors.

 

Single skin panel

Metal panels are one of the most attractive features of a metal building system, having contributed mightily for the growing popularity of Metal Building. Single skin panels used as roof and wall panels, interior roof and wall liners, partition panels, fascia panels, Soffit panels etc.

Neotech stocks different base metals for the panels as

* Bare Galvalume
* Pre painted Galvalume
* Pre painted & un painted Galvanized steel
* Pre painted & un painted Aluminum

 
 

SPECIFICATION SHEET FOR CURRUGATED ALUMINIUM

   
ALLOY

Aluminium alloy , used in the production profiled roof and wall cladding panels,is A-3105H16  for mill finish and H46 for pre-painted.

MATERIAL PROPERTIES

Yield strength – Min 140 Mpa

Modules of elasticity – 69000 Mpa
Coef. Of linear thermal expansion – 24^6*10 per deg.C
DURABILITY
When exposed to the atmosphere natural aluminium forms a thin layaer protective oxide coating on this surface. Thanks to this composition, the roofing element is adequality protected against corrosion under normal conditions of exposure to atmosphere conditions , especially in coastal and industrial area.
FIRE
Aluminium is classified as a non-combustible material , defined by BS 476: part : 1970. Roof coverings of aluminium alloy are rated EXT AA when tested in accordance with BS 476:  Part 3: 1958
 
 
COMBINING WITH OTHER MATERIAL
   
  These roof covering can come into direct contact with plastic, galvanized steel, high-grade and pre-painted steel and zinc sheets
  Direct contact with ordinary steel, coper, brass and lead should be avoided by introducting a continuous separating element such as a PVC tape of bitumen felt strips or alternatively, painted with zinc chromate or aluminium paint. This also applies to direct contact with mortar and concrete.
   
  Timber parts which come into contact with aluminium should be treated with impregnating agents which do not contain copper slats, mercury salts, phenol compounds or fluorine compounds.
   
MILL FINISH
  This is the natural untreated surface of the metal as it leaves the mill.
   
STUCCO EMBOSSED
 

Stucco-embossed aluminium is mill finished aluminium. This is roller-embossed to produce an irregular raised pattern finish. The advantage of embossing is that direct reflections and sun glaze are diffused, without reduction in the total reflectivity.

   

POLYESTER COLOUR–COATED

 

An economical, long life coated, factory applied polyester on the exposed side, and a lacquer coating on the reverse side. This is available in RAL as well as BS colour shades. External side coated in 20-25 microns polyester and Internal side coated in 5-7 microns primer.

   

PVF2 COLOUR-COATED

 

Excellent U.V. resistant, long-life coating of 2 coats of factory applied PVF2 on the exposed side and a lacquer coating on the reverse side. Available in RAL as well as BS colour shades.

 
 
 
 
 
SPECIFICATION FOR CORRUGATED STEEL
   

ALLOY

 

The base material shall confirm to ASTM-A653 (Lock Forming Quality ) or structural quality ASTM-A446 Grade D (Yield strength of Mpa) subject to availability.

   
FINISGHES
  The base steel material shall be hot dipped galvanized Zink coated thickness as per ASTM A525-G90 (Zinc coated 275/m2 total both sides ) subject to availability.
   
AL-Zn COATED
  The base material shall be coated in AZ150 (a50/m2 of aluminium Zinc coated)  confirming to ASTM A792 Grade 50B with minimum yield strength 345Mpa. This coating offers corrosion resistance.
 
PAINT FINISHES

(Applies for galvanized as well as Alu-Zinc)

POLYESTER
An economical long life coating . External side coated in 20-25 microns polyester and  internal side coated in 5-7 microns primer.
PVF2
This coating has high resistance to fading due to excellent UV resistance. Availabile in BS and RAL color shades.
PVC PLASTISOL
This coating has excellent resistance to flaking and has good anti-fading properties. This coating used in a thickness of 200 microns.
   
 
 
 
 
Features
Equipped with modern technology
Economical -1,012/1.000 mm covering width
Any length , 14 meters width of 1.012 mm
Superb thermal insulation
Environment friendly
Cost efficient
Tough, reliable and guaranteed
High quality, light weight, and easy to install
Innovative manufacturing allows panels to be constructed to fit any dimension
Delivery is on time and budget

Polyurethane

Average Density : 35kg/M3  to 40Kg/M3

Thickness : 25mm to 100mm

 
PU THICKNESS
W/M2oC
25mm
.76
35mm
.54
50mm
.38
   
HIGHLIGHTS FOR COMPOSITE PANELS
   

Composite panels are produced using rigid Polyurethane/ Polyisocynerate with external and internal sheets in steel or aluminium of various thickness, coating and colors.

   
OUTSTANDING INSULATING PROPERTIES
  Low thermal conductivity due to chemical structure of Polyurethane/PIR
   
LOW DEAD LOAD
  Due to the combination of lightweight materials
   
CAPABLE OF LONG SPANES
  Fully bonded panels allow even longer spanes
   
PAINTED MATERIAL
  Available in a wide range of standard colours. Extensive choice RAL Colourcoat finishes and colours
   
SIMPLE AND FAST ERECTION
  Factory injected panel (no assembling on site). Easy handling due to low   weight
   
MANFACTURED IN THE INDIA
 

Precise production, accuracy and control. Considerable savings in transportation costs.

               
   
THERMAL INSULATION
 

Effective protection of the thermal insulation against interstitial condensation Thermal insulation efficiency of economically unmatched standards 25 mm to 150 mm depths.

         
   
MATERIAL DELIVERY
  Dependable delivery  dates – Due to speed of manufactured and delivery procedure
   
   
 
 
  INSULATED COMPOSITE PANEL
  GENERAL FEATURES
  MECHANICAL CHARACTERISTICS OF THE FOAM
  ( At a density of 35- 37 kg/m3)
   
  Maximum tensile stress : kg – 4.00/cm2
  Compression resistance : kg – 2.00/cm2
  Sheer resistance : kg – 1.40/cm2
  Flame Spread Index : 25 & 20
  Smoke Develop rate : 450
   
   
  INSULATING CAPACITY
  Between 0.020 to 0.022 Kcal/2mh ˚C as a K value, The U- value for 35,50 & 100mm thick insulated panel, is as follows:
  For 35mm = 0.57 W/m2 oC
  For 50mm = 0.4 W/M2 oC
  For 100mm = 0.2 W/m2 oC
   
  Water absorption of the foam
  After 24 Hours : 1.0% of volume
   
  Close cells
  93%
   
  Self Extinguishing type
  -As per ASTM D 169/68 norms